Polyvinyl alcohol (PVA) resin is a high molecular polymer with a chemical formula of (CH2CHOH)n. It is a commonly used adhesive with good film forming properties, bonding properties and thermal stability. Its water solubility is related to the degree of alcoholysis. When the degree of alcoholysis is below 88%, polyvinyl alcohol can be dissolved in normal temperature water; when the degree of alcoholysis reaches 97%, hot water of 60-80 degrees C should be required for dissolution.
| Specification | Hydrolysis
(mol%) |
Viscosity
(cps) |
Volatiles
(%) |
Ash content(%) | PH |
| 1788 | 86.0-89.0 | 20.0-26.0 | Max 7.0 | Max 7.0 | 5-7 |
| 2488 | 86.0-89.0 | 44.0-52.0 | Max 7.0 | Max 7.0 | 5-7 |
Physical properties
Appearance: white free-flowing powder, odorless and tasteless.
Solubility: Polyvinyl alcohol powder (PVA) 17-88 and 24-88 type are partially alcoholy-soluble types which can be soluble in room temperature water. It is prohibited to use when the temperature drops to below 0 degree C; when the temperature is below 10 degrees C, sufficient dissolution time is required for dissolution, usually takes 5-10 minutes.
Solution stability: Aqueous solution of low viscosity Polyvinyl alcohol is stable at room temperature and does not deteriorate during storage.
Film Formability: Due to the high adhesion strength between Polyvinyl alcohol molecules, Polyvinyl alcohol is easy to form a film, which has colorless and transparent smooth surface with high mechanical strength and good solvent resistance.
Application field
1, Polyvinyl alcohol can be applied in a variety of wall putty, drymix mortar, gypsum products, tile adhesive. It can effectively increase the adhesion of cement, ash calcium powder and gypsum. It can increase fluidity and slow the surface drying time to prevent product surface from cracking. It is suitable for wall/ceiling finishes and tile pastes.
2, adding 1-2KG of Polyvinyl alcohol with fineness above 300 meshes, into the latex paint production process, can effectively improve the smoothness of the product, improve the film formation and reduce the amount of emulsion used 5-10KG.
3, in the thermal insulation mortar system, 1 KG of Polyvinyl alcohol (160 mesh) has the similar effect of 4-5KG latex powder. In practical application, combine latex powder and Polyvinyl alcohol to use will achieve a better effect.
SIDLEYCHEM has focused on the application development and product promotion of construction chemicals such as mortars and coating additives for many years. To provide customers with professional, customized one-stop product supply services and systemized solutions. At present, it has formed fields covering mortar, paint and daily chemicals.
SIDLEYCHEM has the production base in Shandong, China with an annual production capacity of 15,000MT of MC (HPMC/MHEC); 5000 MT of HEC; 10000MT of RDP; 10000MT of PAC for oildrilling; 15000MT of Calcium Formate/Sodium Formate/Potassium Formate etc.
As one of the best suppliers of mortar additives in China, Sidleychem has its own technology center to assist customers in product analysis, product development, formulation optimization and more. At the same time providing the most competitive products, providing customers with the best customized service is our goal.
Packing & Shipping:
In 25kg paper bags inner with PE bags
20'FCL:14 tons with pallets or 16 tons without pallets
Storage &Transportation:
-No Damage during the transportation;
- Protect from Humidity, Rain, Sunlight, Damp and wet;
-Put in dry and ventilated Place During storage;
- Remind must be promptly sealed and packed to prohibit from wet.
){kind=link}