Good Hydrophilia Cellulose Fiber for Improve The Workability of Fresh Fiber Concrete

• Customization: Available
• Type: Cellulose Fiber
• After-sales Service: Technical Services
• Transport Package: Bag
• Specification: 9kg/bag or 10kg/bag
• Trademark: Sidleychem
• Origin: China
• Production Capacity: 5000ton/Year

Product Description

Cellulose fiber, with natural hydrophilicity and high strength, is made of a unique plant species in the alpine region through a series of specific chemical treatments and mechanical processing. Since it belongs to the natural division of plant cells and the growth is not artificial, which gives the surface a firm grip. In the follow-up processing, the fiber is made into a sheet-like monomer using a unique electrodeless material, which is convenient for transporting and delivering the thread. Then, under immersion in water and the mixer's friction, the flaky monomers are easily dispersed into fiber monofilaments, thereby playing an anti-cracking effect, which can effectively improve the mechanical properties of concrete, such as freeze-thaw resistance and impermeability.
 Performance characteristics of cellulose fiber added to the concrete
Effectively prevent the occurrence of concrete shrinkage cracks: due to the characteristics of cellulose fiber itself, such as natural hydrophilicity, excellent grip strength, huge fiber-specific surface area, and high toughness and strength. In addition, under the soaking of water and the action of external force, a large number of evenly distributed fine fibers are formed after being added to concrete, which can effectively prevent the plastic shrinkage of concrete, dry shrinkage, and temperature changes that cause cracks.
Specifications and dosage
Specifications: The fibers are short and thin, so it is not convenient for storage and transportation, generally they are made into flat cubes.
Dosage in concrete: 0.5-1kg

Technical Indicator

(g/cm³) proportion	1.0-1.2	(um) diameter	15-20
(mm) length	2-3	(MPa) strength of extension	500-1000
(GPa) elasticity modulus	8-10	(cm²/g) specific surface area	20000-30000
(μm)   Fiber spacing	500-700(0.9kg/m³) (The dosage is 0.9kg/m³)	Number of fibers (100 million)	12-15(0.9kg/m³) 12-15 (add 0.9kg/m³ per cubic concrete)
hydrophilia	good	bond stress	strong
security	non-poisonous	acid-base resistance property	(95%) Strong (strong retention rate not less than 95%)